Konbyen se ferrotitanium pou chak kg jodi a?

Ki sa ki materyèl yo anvan tout koreksyon pou pwodiksyon endistriyèl nanferrotitanium?

Materyèl yo anvan tout koreksyon pou pwodiksyon endistriyèl nan ferotitanium gen ladan ilmenit konsantre (Fe-TiO3), rutile (TiO2), gaz Titàn (TiO2) ak bouyon Titàn metal (Ti, Ti-V-al, elatriye {{6} Ferrotitanium ak Titàn alyaj .

TiO2 is an oxide that is difficult to reduce. Reducing TiO2 with carbon can only be achieved at high temperatures, and TiC is generated instead of Ti. High-carbon ferrotitanium is obtained. Reducing TiO2 with silicon is not possible, but adding CaO as a flux can promote the silicon reduction reyaksyon .

Titanium and silicon form stable silicides, which are beneficial to the silicon reduction reaction, but the produced ferrotitanium contains a high silicon content. It is possible to reduce TiO2 with aluminum to generate Ti. However, if the aluminum content is lower than the stoichiometric value, a large amount of TiO is pwodwi .

TiO is more stable than TiO2 and cannot be reduced with aluminum. It is a strong alkaline oxide that can form slag with Al2O3 or SiO2. Therefore, CaO should be added to prevent the slag formation reaction of TiO, and it is also beneficial to the reduction of TiO2. Comparing the reaction in Figure 2, it is easier to reduce Ilmenite (Fetio3) ak aliminyòm pase diminye TiO2, ak ajoute CaO gen menm efè a .

Se poutèt sa, diminye Titàn konsantre ak aliminyòm se metòd prensipal la pou pwodwi ferrotitanium . pwodwi a jwenn gen kontni kabòn ki ba, men segondè aliminyòm ak silisyòm kontni . ki baze sou analiz la pi wo a, metòd prensipal yo pou pwodwi ferrotanium yo se allinothermicalments, elektwomik metòd, elektwomik. kòm renovasyon nan bouyon Titàn metal .

Konbyen se ferrotitanium pou chak kg jodi a?

Ferrotitanium (Yuan/tòn): Ferro pri Titàn pou chak kg

Non pwodwi	Spesifikasyon	Pri tranzaksyon yè a	Pri tranzaksyon jodi a	Leve non epi tonbe	Remake
Ba Titàn ferro	30%	12000-12300	12000-12300	-	Pri ki gen ladan taks, (25 pri baz)
Ferrotitanium	40%	12000-12300	12000-12300	-	Pri ki gen ladan taks, (25 pri baz)
Segondè fè Titàn	70%A	28300-29300	28300-29300	-	Pri ki gen ladan taks, (aktyèl pwa)

Sityasyon soti nan manifaktirè endikap nan fè ki ba-Titanium nan pi gwo rejyon yo nan Lachin: pri ferotitanium

Non pwodwi	Spesifikasyon	Pri (Yuan/tòn, 25 pri baz)	Leve non epi tonbe	zòn	Remake
Ba Titàn ferro	30	12200-12500	--	Jiangsu	Pri ki gen ladan taks
Ba Titàn ferro	30	12200-12500	--	Yingkou	Pri ki gen ladan taks
Ba Titàn ferro	30	12200-12500	--	Jinzhou	Pri ki gen ladan taks
Ba Titàn ferro	30	12200-12500	--	Henan	Pri ki gen ladan taks
Ba Titàn ferro	30	12200-12500	--	Changzhou	Pri ki gen ladan taks

Pri nan manifaktirè endikap nan mwayen ak segondè ferotitanium nan pi gwo rejyon nan Lachin: Ferro pri Titàn

Non pwodwi	Spesifikasyon	Pri (Yuan/tòn, 25 pri baz)	Leve non epi tonbe	zòn	Remake
Ferrotitanium	40	12200-12500	--	Jinzhou	Pri ki gen ladan taks
Ferrotitanium	40	12200-12500	--	Henan	Pri ki gen ladan taks
Ferrotitanium	40	12200-12500	--	Jiangsu	Pri ki gen ladan taks
Segondè fè Titàn	Bouyon kalite Titàn	28500-30000	--	Jiangsu	Pri ki gen ladan taks
Segondè fè Titàn	Bouyon kalite Titàn	28500-30000	--	Liaoning	Pri ki gen ladan taks
Segondè fè Titàn	Bouyon kalite Titàn	28500-30000	--	Henan	Pri ki gen ladan taks

Dènye pri tranzaksyon nan mache Chinwa a (pou referans sèlman): Ferro pri Titàn

Non pwodwi	Spesifikasyon	Pri (Yuan/tòn)	Leve non epi tonbe	zòn	Remake
Ba Titàn ferro	30	12000-12300 (25 pri baz)	--	Liaoning	Pri ki gen ladan taks
Ferrotitanium	40	12000-12300 (25 pri baz)	--	Liaoning	Pri ki gen ladan taks
Segondè fè Titàn	70A	28300-29300 (pwa aktyèl)	--	Liaoning	Pri ki gen ladan taks
Segondè fè Titàn	70B	27300-28300 (pwa aktyèl)	--	Liaoning	Pri ki gen ladan taks